The Effect of Gas Nitriding on Wear of Drill Bits during Particle Board Drilling
Porankiewicz Bolesław *, Małdziński Leszek 1, Wieloch Grzegorz 2
1Poznań University of Technology, Poland
2University of Life Science Poznań, Poland
*e-mail: poranek@amu.edu.pl
Received:
(Received: 10 February 2012; accepted: 5 June 2012; published online: 3 September 2012)
DOI: 10.12921/cmst.2012.18.02.103-109
OAI: oai:lib.psnc.pl:416
Abstract:
In this paper multi-factor, non-linear, statistical dependencies between drill bit side edges recession VBKF (mm) and drill bit diameter recession ΔDD (mm) upon cutting path LC (m), and thickness tN (μm) of a nitrided coating layer after drilling coated particle board are determined. Significant influences of the cutting path LC, and the thickness tN of the gas nitrided coating layer together with an interaction on the VBKF and the ΔDD are evidenced. Dependency between hole edge swelling SW (mm) and drill bit side edges recession VBKF is also evaluated.
Key words:
boring; particle board, drill bit diameter recession; hole edge swelling, nitrided coating kayer, side edges recession, spiral drill bit
References:
[1] P. Beer, S. Miklaszewski, A. Sokołowska, Tribological Properties of Wood. Proc. of 10 Jubilee International Summer School, Mielno’98, Koszalin, Poland, 141-160 (1998).
[2] L. Chekour, C. Nouveau, C. Chala, M.-A. Djouadi, Duplex treatment of 32CrMoV13 steel by ionic nitriding and triode sputtering: application to wood machining. Wear 255, 1438-1443 (2003).
[3] B. Porankiewicz, Tępienie się ostrzy i jakość przedmiotu obrabianego w skrawaniu płyt wiórowych. Printing House, Agricultural University of Poznań, 341 (2003).
[4] A. Sokołowska, P. Beer, J. Rudnicki, Niskotemperaturowe azotowanie jarzeniowe noży do produkcji łuszczki. Problemy Eksploatacji, 2, 359-366 (2000).
[5] W. Szymański, Badania wpływu grubości warstwy azotowanej na trwałość wierteł ze stali szybkotnącej przy wierceniu płyt wiórowych. Akademia Rolnicza w Poznaniu, Instytut Podstaw Techniki, Master thesis (1977).
[6] W. Szymański, B. Porankiewicz, L. Małdziński, Wpływ azotowania gazowego na trwałość wierteł do drewna. Roczniki Akademii
In this paper multi-factor, non-linear, statistical dependencies between drill bit side edges recession VBKF (mm) and drill bit diameter recession ΔDD (mm) upon cutting path LC (m), and thickness tN (μm) of a nitrided coating layer after drilling coated particle board are determined. Significant influences of the cutting path LC, and the thickness tN of the gas nitrided coating layer together with an interaction on the VBKF and the ΔDD are evidenced. Dependency between hole edge swelling SW (mm) and drill bit side edges recession VBKF is also evaluated.
Key words:
boring; particle board, drill bit diameter recession; hole edge swelling, nitrided coating kayer, side edges recession, spiral drill bit
References:
[1] P. Beer, S. Miklaszewski, A. Sokołowska, Tribological Properties of Wood. Proc. of 10 Jubilee International Summer School, Mielno’98, Koszalin, Poland, 141-160 (1998).
[2] L. Chekour, C. Nouveau, C. Chala, M.-A. Djouadi, Duplex treatment of 32CrMoV13 steel by ionic nitriding and triode sputtering: application to wood machining. Wear 255, 1438-1443 (2003).
[3] B. Porankiewicz, Tępienie się ostrzy i jakość przedmiotu obrabianego w skrawaniu płyt wiórowych. Printing House, Agricultural University of Poznań, 341 (2003).
[4] A. Sokołowska, P. Beer, J. Rudnicki, Niskotemperaturowe azotowanie jarzeniowe noży do produkcji łuszczki. Problemy Eksploatacji, 2, 359-366 (2000).
[5] W. Szymański, Badania wpływu grubości warstwy azotowanej na trwałość wierteł ze stali szybkotnącej przy wierceniu płyt wiórowych. Akademia Rolnicza w Poznaniu, Instytut Podstaw Techniki, Master thesis (1977).
[6] W. Szymański, B. Porankiewicz, L. Małdziński, Wpływ azotowania gazowego na trwałość wierteł do drewna. Roczniki Akademii